Precision Stainless Steel Strip from China, Precision Stainless Steel Strip Manufacturer & Supplier

Precision Stainless Steel Strip

We are one of the world's leading manufacturers of precision steel strip. Our cold rolling mills can produce precision steel strip with a minimum thickness of 0.04 mm (0.0016 inches), a minimum stable supply thickness of 0.05 mm (0.0020 inches), a minimum tolerance of +/-0.002 mm (0.00007 inches) and a maximum width of 700mm (27.5591inches).

Material types:

430
Japanese Standard	DSM	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Bend	Density/20℃ Kg/dm3
SUS430	430	0.12	1	0.04	0.03	1	16.00-18.00	0.75	420	205	22	183	89	200	180	7.7

410SC/0Cr13Mn
DSM	C %	Si≤%	Mn %	P≤%	S≤%	Cr %	Ni≤%	N %	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness
DSM	C %	Si≤%	Mn %	P≤%	S≤%	Cr %	Ni≤%	N %	Mpa	Mpa	50mm	HBW	HRB	HV
410SC	0.08-0.12	0.4-0.8	0.7-1.0	0.035	0.01	11.50-12.50	0.6		450	205	15	229	98	241
0Cr13Mn	0.045-0.08	0.6	1.0-2.5	0.035	0.03	11.50-14.50	0.6	0.008-0.020	410	205	20		93

410S/410
Japanese Standard	DSM	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Bend	Density/20℃ Kg/dm3
SUS410S	06Cr13	0.08	1	0.04	0.03	1	11.5-13.5	0.6	440	205	20	201	93	210	180	7.75
SUS410	12Cr13	0.15	1	0.04	0.03	1	11.5-13.5	0.6	440	205	20	201	93	210	180	7.7

422

DSM

C %

Si %

Mn %

P≤%

S≤%

Cr %

Mo %

Min
Tensile strength

Min
Yield
strength

Min
Elongation
%

Max hardness

Mpa

50mm

HBW

HRB

TMS422

0.36-0.40

0.30-0.50

0.45-0.65

0.025

0.01

13.20-14.00

0.90-1.10

590

330

420J1/420U6
Japanese Standard	DSM	C %	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	N %	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Density/20℃ Kg/dm3
Japanese Standard	DSM	C %	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	N %	Mpa	Mpa	50mm	HBW	HRB	HV	Density/20℃ Kg/dm3
SUS420J1	20Cr13	0.16-0.25	1	0.04	0.03	1	12.00-14.00	0.6		520	225	18	223	97	234	7.75
	420U6	0.13-0.25	1	0.04	0.03	1	13.00-14.50	0.6	0.06-0.12	520	225	18	223	97	234	7.75

40Cr13/420J2
European Standard	Chinese Standard	C %	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness
European Standard	Chinese Standard	C %	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	Mpa	Mpa	50mm	HRB	HV
1.4031		0.36-0.42	1	0.04	0.015	1	12.5-14.0		max 760	205	12	98	240
1.4034		0.43-0.5	1	0.04	0.015	1	12.5-14.5		Max 780	205	12	99	245
	40Cr13	0.36-0.45	0.8	0.04	0.03	0.8	12.0-14.0	0.6	590	225	15
1.4028	30Cr13	0.26-0.35	1	0.04	0.03	1	12.0-14.0	0.6	540	225	18	99	247

50Cr15MoV/1.4116

European
Standard

DSM

C %

Mn≤%

P≤%

S≤%

Si≤%

Cr %

Mo %

V %

Min
Tensile strength

Min
Yield
strength

Min
Elongation
%

Max hardness

Mpa

50mm

HBW

HRB

1.4116

50Cr15MoV

0.45-0.55

0.04

0.015

14.00-15.00

0.50-0.80

0.10-0.20

850

280

100

280

409L
Japanese Standard	Chinese Standard	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	N≤%	Others	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Bend	Density/20℃ Kg/dm3
Japanese Standard	Chinese Standard	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	N≤%	Others	Mpa	Mpa	50mm	HBW	HRB	HV	Bend	Density/20℃ Kg/dm3
SUH409L		0.03	1	0.04	0.03	1	10.50-11.75	0.6		Ti:6(C-0.75)	360	175	25	162	80	175	180	7.75
	0.22Cr11Ti	0.03	1	0.04	0.02	1	10.50-11.75	0.6	0.03	Ti:0.15-0.5 Ti≥8(C+N); Nb:0.10	380	170	20	179	88	200	180	7.75

6Cr13

DSM

C %

Mn≤%

P≤%

S≤%

Si≤%

Cr %

Min
Tensile strength

Min
Yield
strength

Min
Elongation
%

Max hardness

Mpa

50mm

HBW

HRB

6Cr13

0.6-0.7

0.04

0.03

12.50-14.00

540

301
Japanese Standard	DSM	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni≤%	N≤%	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Density/20℃ Kg/dm3
										Mpa	Mpa	50mm	HBW	HRB	HV
301	301	0.15	2	0.045	0.03	1	16.00-18.00	6.00-8.00	0.1	520	205	40	207	95	218	7.93

Hardness	Min yield strength Mpa	Min strength of extension Mpa	Min ratio of elongation A%			hardness
			＜0.4mm	0.4-0.8mm	≥0.8mm	HV(min)
1/4H	515	860	25	25	25	250
1/2H	760	1035	15	18	18	310
3/4H	930	1205	10	12	12	370
H	965	1275	8	9	9	430
EH	1790	1860				490

304
Japanese Standard	DSM	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni %	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Density/20℃ Kg/dm3
Japanese Standard	DSM	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni %	Mpa	Mpa	50mm	HBW	HRB	HV	Density/20℃ Kg/dm3
SUS304		0.08	2	0.045	0.03	1	18.00-20.00	8.00-10.50	520	205	40	187	90	200	7.93
	304	0.08	2	0.045	0.03	1	17.50-19.50	8.00-10.50	520	205	40	201	92	210	7.93

Hardness	Min yield strength Mpa	Min strength of extension Mpa	Min ratio of elongation A%			hardness
Hardness	Min yield strength Mpa	Min strength of extension Mpa	＜0.4mm	0.4-0.8mm	≥0.8mm	HV(min)
1/2H	515	860	10	10	12	250
3/4H	760	1035	6	7	7	310

321

Japanese Standard

DSM

C≤%

Mn≤%

P≤%

S≤%

Si≤%

Cr %

Ni %

Others

Min
Tensile strength

Min
Yield
strength

Min
Elongation
%

Max hardness

Density/20℃
Kg/dm3

Mpa

50mm

HBW

HRB

SUS321

321

0.08

0.045

0.03

17.00-19.00

9.00-13.00

Ti≥5C

520

205

187

200

8.03

1.4828
European Standard	DSM	C≤%	Mn≤%	P≤%	S≤%	Si≤%	Cr %	Ni %	N≤%	Min Tensile strength	Min Yield strength	Min Elongation %	Max hardness			Density/20℃ Kg/dm3
										Mpa	Mpa	50mm	HBW	HRB	HV
1.4828	1.4828	0.2	2	0.045	0.015	1.5-2.5	19.00-21.00	11.00-13.00	0.11	550-750	230	28	223			7.98

316L

USS

DSM

C≤%

Mn≤%

P≤%

S≤%

Si≤%

Cr %

Ni %

N≤%

Mo %

Min
Tensile strength

Min
Yield
strength

Min
Elongation
%

Max hardness

Density/20℃
Kg/dm3

Mpa

50mm

HBW

HRB

316L

0.03

0.045

0.03

16.00-18.00

10.00-14.00

0.1

2.0-3.0

485

170

217

220

7.98